Pure copper
Copper / Brass / C194
We also offer copper coil (C1020, C1100, C1220), brass coil (C2600, C2680), and C194.
Lineup
Item | Chemical composition | Electrical conductivity | Temper | Standard thickness | Tensile strength | Elongation | Vickers hardness | |
---|---|---|---|---|---|---|---|---|
[CDA No.] | [wt%] | [%IACS] | [mm] | [N/mm2] | [%] | [HV] | ||
Oxygen-free copper | C10200 | Cu:99.96 Min. | 101 | O | 0.20-4.00 | 195 Min. | 30 Min. | 65 Max. |
1/4H | 0.20-4.00 | 215-275 | 20 Min. | 55-100 | ||||
1/2H | 0.20-3.50 | 245-315 | 10 Min. | 75-120 | ||||
H | 0.15-3.50 | 275 Min. | – | 80 Min. | ||||
Tough pitch copper | C11000 | Cu:99.90 Min. | 101 | O | 0.20-4.00 | 195 Min. | 30 Min. | 65 Max. |
1/4H | 0.20-4.00 | 215-275 | 20 Min. | 55-100 | ||||
1/2H | 0.20-3.50 | 245-315 | 10 Min. | 75-120 | ||||
H | 0.15-3.50 | 275 Min. | – | 80 Min. | ||||
Phosphorus deoxidized copper | C12200 | Cu:99.90 Min. P:0.025 |
85 | O | 0.20-4.00 | 195 Min. | 30 Min. | 65 Max. |
1/4H | 0.20-4.00 | 215-275 | 20 Min. | 55-100 | ||||
1/2H | 0.20-3.50 | 245-315 | 10 Min. | 75-120 | ||||
H | 0.15-3.50 | 275 Min. | – | 80 Min. | ||||
C2600 (Cu-30Zn) |
C26000 | Cu:70.0 Zn:Rem. |
28 | O | 0.20-3.50 | 275 Min. | 35 Min. | 90 Max. |
1/4H | 0.20-3.50 | 325-410 | 30 Min. | 75-125 | ||||
1/2H | 0.20-3.50 | 355-440 | 23 Min. | 85-145 | ||||
H | 0.15-3.00 | 410-540 | 10 Min. | 105-175 | ||||
EH | 0.15-3.00 | 520-620 | 5 Min. | 145-195 | ||||
SH | 0.15-3.00 | 570-670 | 3 Min. | 165-215 | ||||
ESH | 0.15-3.00 | 620 Min. | – | 180 Min. | ||||
C2680 (Cu-35Zn) |
C26800 | Cu:65.0 Zn:Rem. |
27 | O | 0.20-3.50 | 275 Min. | 35 Min. | 90 Max. |
1/4H | 0.20-3.50 | 325-410 | 30 Min. | 75-125 | ||||
1/2H | 0.20-3.50 | 355-440 | 23 Min. | 75-145 | ||||
H | 0.15-3.00 | 410-540 | 10 Min. | 105-175 | ||||
EH | 0.15-3.00 | 520-620 | 5 Min. | 145-195 | ||||
SH | 0.15-3.00 | 570-670 | 3 Min. | 165-215 | ||||
ESH | 0.15-3.00 | 620 Min. | – | 180 Min. | ||||
C194 | C19400 | Cu:Rem. Fe:2.35 P:0.07 Zn:0.12 |
60 Min. | 1/2H | – | 373-412 | 12 Min. | 115-135 |
H | – | 414-482 | 3 Min. | 125-145 | ||||
EH | – | 462-503 | 2 Min. | 135-150 | ||||
SH | – | 482-524 | – | 140-155 | ||||
ESH | – | 531-573 | – | 150-165 | ||||
50 Min. | SSH | – | 551 Min. | – | 155 Min. |
*Please note that the values in the table are reference values and are subject to change without notice.