DSC-3N
Related standardsJASO JC100
ApplicationsHeat sink bases, heat spreaders, high current terminals, busbars, lead frames, etc.
Copper alloy that is superior in strength and heat resistance to pure copper.
Ideal for heat sink bases, high current terminals, busbars, etc.
DSC-3N (DOWA Super Copper) is a 99.9% copper alloy containing trace amounts of additive elements.
It has better strength and heat resistance than C1020. It also has high thermal conductivity (350 W/m･K and higher).
DSC-3N is a low-cost alloy and provides good balance of characteristics, suitable for high current terminals, busbars and thermal devices such as heat sink bases.
Chemical composition
[wt%]
| Fe + Ni + Sn + Zn + P | Cu | |
|---|---|---|
| Typical values | 0.1 | 99.9 |
Physical properties
| Melting point [℃] | 1080 |
|---|---|
| Density [g/cm3@20℃] | 8.9 |
| Thermal expansion coefficient [10-6/K@20-300℃] |
17.7 |
| Thermal conductivity [W/m・K@20℃] |
355 |
| Electrical conductivity [%IACS@20℃] |
92 |
| Young’s modulus [kN/mm2] | 122 |
| Poisson’s ratio | 0.33 |
Mechanical properties
| Temper | Tensile strength [N/mm2] |
0.2 % yield strength (typical value) [N/mm2] |
Elongation [%] |
Vickers hardness [HV] |
|---|---|---|---|---|
| O | 250-320 | 140 | 30 Min. | 90 Max. |
| 1/4H | 280-350 | 280 | 15 Min. | 90-120 |
| 1/2H | 320-390 | 340 | 8 Min. | 100-130 |
| H | 370-440 | 380 | 5 Min. | 110-140 |
| EH | 400 Min. | 450 | 3 Min. | 120 Min. |
Bending workability (W bend, bending width=10mm)
| Temper | MBR/t | |
|---|---|---|
| Good Way | Bad Way | |
| 1/2H | 0 | 0 |
| H | 0 | 0 |
| EH | 0 | 0 |
*Please note that the values in the table are reference values and are subject to change without notice.